UP-101 Mo (S3Mo)
SAW (submerged arc welding) wires for mild and low alloyed steels

Classification DIN EN ISO

14171-A S3Mo, 24598-A S S MnMo

Material No.

1.5426

Classification AWS

A5.23 EA4

Approvals

TÜV 03275, CE, DB 52.045.08

Characteristics and application

Submerged arc welding wire for 0.5%Mo steels, i.e. P1. These steels are commonly used at service temperatures up to 500°C and for some sub-zero structural applications. The 0.5% alloying improves creep performance compared to CMn steels and sees the alloy being used for boiler, pressure vessel and piping construction. The good general mechanical properties also ensures use in general structural engineering applications.

Base materials

For similar alloyed high temperature steels and cast steels, ageing resistant and steels resistant to caustic cracking.
S550GD, S355J0, E335, P285NH, P310GH, S355J0Cu, P355N-P460N, P355NH-P460NH, 16Mo3
ASTM: A182/A336 grade F1, A204 grades A/B/C, A209/A250 grade T1, A217 grade WC1, A335 grade P1, A352 grade LC1

Typical analysis in %

C: 0,12
Si: 0,15
Mn: 1,52
Mo: 0,52

Yield strength in Mpa

≥470

Tensile strength in Mpa

≥550

Elongation in %

4d/5d: ≥20/22

Typical heat treatment

Preheat temperature: Dependent on material thickness
Interpass temperature: max. 250°C
PWHT: AW or 650°C

Other products

SAW: UP-100 Mo (S2Mo)
MIG/GMAW: ED-SG Mo
TIG/GTAW: WSG Mo
Gas welding: U 47 Mo (G IV)